| No. | Pasipatan résin | nilai has | Unit | Métode Tés |
| 1 | Gravitasi spésifik, 23 ℃ | 1.05 | g/cm³ | ASTM D792 |
| 2 | Kapang Shrinkage, 23 ℃, 3.2mm, 23 ℃ | 0.4-0.7 | % | ASTM D955 |
| 3 | Ngalembereh Laju Aliran, 220 ℃, 10kg | 22 | g/10 mnt | ASTM D1238 |
| 4 | Kakuatan Tensile dina ngahasilkeun, 23 ℃, 50mm / mnt, 3.2mm | 49 | MPa | ASTM D638 |
| 5 | Elongation Tensile dina ngahasilkeun, 23 ℃, 50mm / mnt, 3.2mm | 5 | %, (Min) | ASTM D638 |
| 6 | Elongation Tensile dina putus, 23' ℃, 50mm / mnt, 3.2mm | 10 | %, (Min) | ASTM D638 |
| 7 | Modulus Tensile, 23 ℃, 50mm / mnt, 3.2mm | 2350 | MPa | ASTM D638 |
| 8 | Kakuatan Flexural, 23 ℃, 15mm / mnt, 3.2mm | 78 | MPa | ASTM D790 |
| 9 | Modulus lentur, 23 ℃, 15mm / mnt, 3.2mm | 2550 | MPa | ASTM D790 |
| 10 | Kakuatan Dampak Izod, Notched, 3.2mm, 23 ℃ | 220 | J/m | ASTM D256 |
| 11 | Kakuatan Dampak Izod, Notched, 3.2mm, -30 ℃ | 90 | J/m | ASTM D256 |
| 12 | Kakuatan Dampak Izod, Notched, 6.4mm, 23 ℃ | 220 | J/m | ASTM D256 |
| 13 | Kakuatan Dampak Izod, Notched, 6.4mm, -30 ℃ | 90 | J/m | ASTM D256 |
| 14 | Rockwell karasa, R-Skala | 110 | / | ASTM D785 |
| 15 | HDT, Edgewise, 1.82MPa, 6.4mm, Unannealed | 85 | °C | ASTM D648 |
| 16 | VICAT, 50N, 50 ℃/jam | 92 | °C | ASTM D1525 |
| 17 | RTI Éléktronik | 95 | °C | UL 746B |
| 18 | RTI Mechanical kalawan Dampak | 95 | °C | UL 746B |
| 19 | RTI Mékanis tanpa Dampak | 95 | °C | UL 746B |
| 20 | Kaduruk, 1,5 mm | HB | / | UL 94 |
| 21 | Kaduruk, 3.0mm | HB | / | UL 94 |
